Carbide Insert efficiency development of this research equivalent to standard insert type : SEKN1203AFTN. For the higher operating efficiency is the machining time by the tool life increased for rough machine of face milling machine. Flank designed to have a flow slot coolant flow rate of coolant to have a incrased convenient flow as a result the surface and cutting edges less heat. The machining ability is different compared to the unslot in flank. The flank slot reduces the contact and slot which to have coolant flow and friction force milling machining. As a result the milling time was 26.31% the vibration was reduced by 35% and the workpiece surface Roughness was reduced 62.79%. As a result to development the phototype product is performance in using and cutting edge increased. It can be apply in using Cement Tungsten Carbide in sustainable industries.

WC powder was obtained from recycling cemented carbide scraps. This metal power contained tungsten carbide (WC) at 89.17% titanium (Ti) at 4.90% tantalum (Ta) at 3.56% niobium (Nb) at 1.31% and molybdenum (Mo) at 0.93%. Its particle size and distribution was in the range of 0.03-85.31 µm. After quality improvement of the metal powder by ball milling screening and separating the compounds the result showed that the particle size of the metal powder was decreased to 0.01-0.10 µm (10-100 nm). The average size of the powdered particle was 28 nm. The tungsten powder was in more perfect condition by 95.85%

This study developed the cemented tungsten carbide by steadily sintering at 1430 °C for one hour. The tungsten carbide structure is a long shape. Its grain size has a difference between width and length and there are high distribution of sizes and shapes. In comparison with the work piece which has the similar size of grain structure the milling duration of tungsten carbide is less even though the condition of WC-Co is the same (95% WC – 5% Co). When the sintering of 1400 °C with the identical milling duration is performed. It turned out that both grain structures of the tungsten carbide and the work piece are similar and their grain sizes are slightly different. However when the grain structures are almost the same and sphericity is increased the hardness and wear resistance will also be improved. Therefore the size of grain structure between 1.00 – 3.00 μm with the milling duration of 100 hours will provide a work piece that has a wear resistance according to international standard