This research aims to produce the T-BAR particleboard from Physic nuts for interior building which are brought agricultural wastes to used for beneficial materials. Under the Thailand industrial standard (TIS-876-2547) specified the evaluated values such as desnsity water content water absorption thickness swelling bending strength elastic modulus and internal bonded. The experiment and evaluation processes between Physic nuts per Urea Formaldehyde ratio and Physic nuts per Phenol-cyanate based on 90:10 92:8 95:5 and 97:3 in consequence that we found the thickness of particleboard not more than 2 cm. The suitable ratio for Phenol-cyanate 92:8 percentage (Physic nuts 92% with Phenol-cyanate 8%) and suitable ratio for Urea Formaldehyde 90:10 percentage (Physic nuts 90% with Urea Formaldehyde 10%) at 120 Celsius temperature on pressing process. The Phenol-cyanate glue ratio of 0.80 gram per cubic centimeter suited to produce the particleboards averaged water content before pressing 8.89% suitable pressure in process 150 pound per square inch water content 7.65% density 0.818 gram per cubic centimeter water absorption 14.23% during 2 hours thickness swelling 8.02% during 2 hours internal bond 0.56 MPa bending strength 21.45 MPa modulus 2116 MPa. The Urea Formaldehyde glue ratio of 0.82 gram per cubic centimeter suited to produce the particleboards averaged water content before pressing 9.84% suitable pressure in process 152 pound per square inch water content 8.63% density 0.833 gram per cubic centimeter water absorption 14.36% during 2 hours thickness swelling 8.95% during 2 hours internal bond 1.39 MPa bending strength 22.37 MPa modulus 2117 MPa. As the results shown that both of Urea Formaldehyde and Phenol-cyanate with Physic nuts passed the TIS 876-2547 standard. The Physic nuts can produce the particleboards for using inside building.

The objective of this research is to produce the T- BAR plate from the agriculture process’s waste. The researcher brought physic nut plant to produce T- BAR plate forint prior building. It was tested based on Thailand industrial standard (TIS 876-2547)which are Determination of moisture content density absorption and expansion when soak in water .For cohesion and perpendicular surface tension and tested for flexural resistance and modulus of elasticity The results show that suitable size material should not thicker than 2 centimeters. The experiment of ratio between physic nut plant and phenol cyanide resin at 90:10 and 92:8. The researcher found that suitable proportion are 92%physic nut pant with 8%phenol cyanide resin. The temperature used for compression was 120 C. The appropriate density to the compression plate was 0.80 g/cm.3 The moisture content of materials before compression was at 8.89% average. The suitable compression was 150 lb/in². The moisture content was at 7.65% The density is at 0.818 g/cm.3expansion value when soaked in water for 2 hours was at 8.02% water absorption retain 2 hour is at 14.23% Inner bond is at 0.56 MPa. Flexibility is at 21.45 MPa. mordulus 2116MPa.Which the result of tested with the Thailand industrial standard (TIS 876-2547).The experiment concluded that we can used physic nut plant as material to make T- BAR plate for interior building.

ในการวิจัยครั้งนี้ มีวัตถุประสงค์เพื่อนาเอาต้นสบู่ดา ไปผลิตเป็นแผ่นผนัง ซึ่งเป็นการนาเศษวัสดุเหลือใช้ทางการเกษตรมาใช้ให้เกิดประโยชน์ ด้วยเหตุนี้ผู้วิจัยจึงเห็นว่าน่าจะนาเอาพืชดังกล่าวไปผลิตเป็นแผ่นผนังภายในอาคารแล้วทดสอบตาม มาตรฐานผลิตภัณฑ์อุตสาหกรรม แผ่นชิ้นไม้อัดชนิดอัดราบ (มอก. 876-2547)ได้แก่ การทดสอบหาค่าความชื้น ความหนาแน่น การดูดซึมและการพองตัวเมื่อแช่น้า หาค่าแรงยึดเหนี่ยวภายใน หรือแรงดึงตั้งฉากกับผิวหน้า และทดสอบหาค่าความต้านทานแรงดัดและมอดูรัสยืดหยุ่น โดยทาการทดลองที่สัดส่วนระหว่างต้นสบู่ดากับกาวยูเรียฟอร์มาลดีไฮล์ที่ 85:15 87:13 89:11 91:9 93:7 และ 95:5 ผลการทดลองพบว่า ขนาดของสบู่ดาที่ใช้อัดขึ้นรูปเป็นแผ่นควรไม่เกิน 2 ซม. สัดส่วนที่เหมาะสม ได้แก่ 89:11 (สัดส่วนระหว่างต้นสบู่ดา 89%ผสมกับกาวยูเรียฟอร์มาลดีไฮล์ 11 %) อุณหภูมิที่ใช้ในการอัดอยู่ที่ 120 องศาเซลเซียส ความหนาแน่นที่เหมาะสมในการอัดแผ่นเท่ากับ 0.80 กรัมต่อลูกบาศก์เซนติเมตร ปริมาณความชื้นก่อนอัดเฉลี่ยอยู่ที่ 8.89% แรงอัดที่เหมาะสมอยู่ที่ 150 ปอนด์ต่อตารางนิ้ว ค่าความชื้นอยู่ 7.64%ค่าความหนาแน่น อยู่ที่ 0.817กรัมต่อลบ.ซม. การพองตัวเมื่อแช่น้าที่ 2 ชม. อยู่ที่ 8.01% การดูดซึมน้าเมื่อแช่น้าที่ 2 ชม อยู่ที่ 14.22% แรงยึดเหนี่ยวภายในอยู่ที่ 0.56 MPa เมกกะปาสคาล ค่าความต้านทานแรงดัด อยู่ที่ 22.36เมกกะปาสคาล(MPa) ค่ามอดุลัสยืดหยุ่นอยู่ที่ 2112 เมกกะปาสคาล (MPa) ซึ่งผลการทดสอบอยู่ในเกณฑ์ตามมาตรฐานผลิตภัณฑ์อุตสาหกรรม แผ่นปาร์ติเคิลบอร์ด (มอก. 876-2547) กล่าวโดยสรุปคือต้นสบู่ดาสามารถนาไปผลิตเป็นแผ่นผนังภายในอาคารได้