Man Lueat (Dioscorea alata) flour is a biopolymer material that can be formed into an edible film. It can be contacted directly with food consumed and naturally biodegraded. The aims of this research were to study the effect of physicochemical mechanical and thermal properties of edible film from Man Lueat flour. The film forming solution was prepared by Man Lueat flour at 4% w/w. The glycerol was used as a plasticizer. It was studied at 3 different levels; 30 40 and 50% w/w of Man Lueat flour. The film forming solutions were formed using the solution casting method and dried at 50 °C for 16 h. Results showed that the glycerol content at different levels of the edible film from Man Lueat flour had no effect on the thickness color transparency and elongation at break. However the moisture content water solubility swelling property and water vapor permeability of the film tended to increase when increasing the glycerol content. In contrast the Young’s modulus and tensile strength of films tended to decrease significantly when the glycerol content increased. Thermal properties were found that decomposition temperature of films occurred 2 stage; the first stage occurs between 50 to 130 ° C and the second stage occurs between 263 to 315 ° C. The analysis of FT-IR showed that the different levels of glycerol affected the structure of the film (3278 cm-1). Therefore the edible film from Man Lueat flour can be applied as a food packaging material to protect the quality of food products.

Riceberry rice is dark purple coloured grains. It is one of the most famous rice for consumers. There are nutrients and high antioxidant properties. Riceberry broken rice (RBR) is a by-product from the rice milling process and has a low value. It can be processed into various products. The purpose of this research was to study the ingredients and the ratios for tablet formulations including RBR powder milk powder whey protein icing sugar strawberry powder bulking agent anticaking agent and lubricant agent. Tabletting of powders was performed using a rotary tablet press machine. It was found that the powder products exhibited passable flow with the Carr Index of 24.57-32.10% and the Hausner Ratio value of 1.33-1.47. The water activity value of product was in the range 0.36-0.45. The tablets had thickness 3.86-4.38 mm diameter 13.07-13.35 mm and weight 0.62-0.71 g/tablet. The increase of RBR powder content (10% - 40%) decreased hardness value of tablet products about 5 times (from 64 N to 12 N). Sensory evaluation of products in appearance color texture odor flavor hardness dissolution in the mouth and overall liking were conducted using 9 - point hedonic scale with 30 untrained panelists. The results showed that the optimal tablet formulation consisted of 30% RBR powder 30% icing sugar 18% milk powder 1% anticaking agent 1% lubricant agent and 20% bulking agent or strawberry powder. They showed the highest overall liking scores in ranges of “like slightly” to “like moderately”