This research is to study the efficiency of treating wastewater from dyeing fabric by the ozonation process. By using rutile TiO2 coated plastic media to catalyze. Which uses O3 generators with a capacity of 2.62 - 3.10 g/hr. By studying the factors that affect the treatment efficiency of COD and color such as the pH of the water used in the treatment at pH 3 pH 7 and pH 11 the initial COD concentration of 100% 50% and 25% which have values in the range of 100 -320 mg/L. O3 exposure time 120 min. From the study it is found that the efficiency of reducing the impurities in wastewater by the ozonation process in the pH 11 state the COD concentration at 50% can reduce the COD. And the maximum color is at 33.3% and 90% from the 550 ADMI color intensity with a COD of 180 mg/L. For the study of the efficiency of reducing the impurities of wastewater by ozonation process together with 2 g. of TiO2/1 L. of wastewater in the condition of pH 11 concentration COD Beginning at 100% with the ability to reduce COD values And the maximum color is at 40% and 80% of the 270 ADMI color intensity with a COD of 190 mg/L. The amount of O3 suitable for treatment has an average value of 0.0374 g/min./10.5 L. of wastewater. The duration of O3 exposure in both processes has a similar approach to the efficiency of COD and color treatment when increasing the duration of O3 exposure.

The objective of this study was implementation of microcontroller to construct Appl to control the operation of the Dog food exchange machine using plastic bottles system. To study an operation control of microcontroller system operation and the to create construction of a Dog food exchange machine using plastic bottles. The component of Dog food exchange machine using plastic bottles are divided into 3 parts: 1) parts of detecting plastic bottles sensor 2) part of the motor control 3) part of the vending machine. Results of the study of Dog food exchange machine using plastic bottles. used in 2 ways: 1) plastic bottle vending 2) coin vending for 10 baht. When the total number of bottles is set at 15 bottles the plastic bottle vending machine will not work until the Reset button is pressed. Can still work normally

This research was concentrated on characterized mechanical properties and adjusted compatibility of poly (lactic acid) (PLA) with thermoplastic starch (TPS) as biodegradable polymers composites. PLA was blended with TPS at the proportion of 10 20 30 50 and 70 wt% as well as 2 phr chain extender by an internal mixer at 200°C. The blended materials were then injection molded at 230°C. Tensile testing showed that as the amount of TPS increase the elongation at break tended to increase but the tensile strength and modulus tended to decrease. The morphology was investigated by scanning electron microscope. It was found that distinct phase between PLA and TPS was observed. Yet adding the chain extender clearly improved the compatibility between PLA and TPS. The blended materials were also analyzed by differential scanning calorimetry method to study thermal properties. It was found that as the amount of TPS increased the glass transition temperature (Tg) melting temperature (Tm) and cold crystallization temperature (Tcc) deceased. Additionally chain extenders did not affect thermal properties. The thermal stability of the composites decreased when increasing the amount of TPS because of the degradation of TPS in PLA. However when heated at 100ºC for 1 hr the PLA sample bent while TPS did not bend. When PLA was mixed with TPS the composite was bent according to adding TPS.

In order to maintain food and materials including drying products at the original dried condition silica gel can be one choice for absorbing moisture. Most silica gel is packed in an Parcel made from plastic which is difficult to naturally degrade thus causing environmental problems. This research therefore have developed packaging material from agricultural waste corn husks for absorbing moisture from food rice. From the study it was found that the corn husk paper had characteristic of smooth paper surface. When making it into a corn fiber Parcel its maximum moisture absorption from saturated humidity was 9.22±0.92% and it could absorb the moisture from the rice stored at room temperature when compared to the plastic sachet at 8.26±0.50% and 9.30±0.08% respectively. When coated with kaffir lime oil extract the corn husk Parcel had the capability in anti-fungus commonly habituated in corn husks up the concentration of 15000 ppm. It could naturally be degraded within 12 days. Therefore with these advantageous qualification the natural Parcel made of corn husk paper harboring silica is for moisture absorption as sustainable and environmental conservation material.

จากการทดลองวิจัยพบว่าดินเป็นชั้นคุณภาพ A4 ประเภทของดินทรายแป้ง (Silty Soils) ผลการขึ้นรูปตามอัตราส่วนของ ดินลูกรัง – พลาสติก-ทราย ดินลูกรังและทรายที่ไมมีเรซินเป็นตัวประสานไมสามารถขึ้นรูปได้ และ ดินลูกรังและทรายที่มีเรซิน น้อยกว่า 20 % ไม่สามารถขึ้นรูปได้เนื่องจากปริมาณตัวประสานไมสามารถยึดเกาะกันระหว่างมวลกับพลาสติก กำลังอัดของ คอมโพสิตพรุน ขนาด 1 CM. สามารรับกำลังอัดตำสุดที่สามารขึ้นรูปและทดสอบได้อยู่ที 0.67 Ksc. และสูงสุดอยู่ที 6.37 Ksc. กำลังอัด คอมโพสิตพรุน ขนาด 2 CM. สามารรับกำลังอัดตำสุดที่สามารขึ้นรูปและทดสอบได้อยู่ที 2.1 Ksc. และสูงสุดอยู่ที 79.1Ksc.คอมโพสิตพรุน ขนาด 3 CM. สามารรับกำลังอัดตำสุดที่สามารขึ้นรูปและทดสอบได้อยู่ที 6.77 Ksc. และสูงสุดอยู่ที 132.03Ksc.คอมโพสิตพรุนขนาด 4 CM. สามารรับกำลังอัดตำสุดที่สามารขึ้นรูปและทดสอบได้อยู่ที 4.6 Ksc. และสูงสุดอยู่ที 138.17Ksc. คอมโพสิตพรุน 5 CM. สามารรับกำลังอัดตำสุดที่สามารขึ้นรูปและทดสอบได้อยู่ที 22.3 Ksc. และสูงสุดอยู่ที 143.20 Ksc.ความสามารถในการดูน้ำความชื่นลดลงตามปริมาณเรซิ่นที่เพิ่มขึ้นตำสุดที่สามารขึ้นรูปและทดสอบได้อยู่ที 0.0%. และสูงสุดอยู่ที 20.02% อ๊อกซีเจนในน้ำ (Dissolved) ของดินคอมโพสิตพรุน ทุกขนาก มีค่ามากกว่า 3 ปลอดภัย นำไปใช้เป็นวัสดุเพิ่มค่า อ๊อกซีเจนในน้ำเลียงสัตว์น้ำได้ อัลคาไลนิตี้ (Total alkalinity) kH ค่าทีน้อยทีสุดได้สูงสุดอยู่ที่ 238 มิลิกรัมต่อลิตร สูงสุดอยู่ที 549 มิลิกรัมต่อลิตร ทุกอัตราส่วนไม่สามารถ ลดค่าแอมโมเนีย (Ammonium) ให้ได้ตามมาตราฐาน ค่า ไนไตรท์ (Nitrite) ทุกอัตราส่วนสามารถ ลด ได้ตามมาตราฐาน ค่า PH กรด-ด่าง (PH indicator strips) เป็นตามมาตราฐาน 6.50-8.50 ค่าอยู่ที่ 7 – 9 ดังนั้นการเลื่อกใช้งานให้เหมาะกับคุณสมบัตของวัสดุแต่ละขนาดและอัตราส่วนผสม