This research study the effect of pozzolanic materials on light weight concrete by replacement cement with fly ash and Meta kaolin which affect the properties of concrete by using pumics aggregate. Coarse in aerated concrete and consider mechanical properties. Aerated concrete replacement cement by fly ash 20% 35% and 50% respectively and meta-kaolin is replaced. From the results it was found that the compressive strength of light weight concrete at 28 days w/b = 0.55 was higher than that of every 14 days of cement and cement cement replacement by fly ash 50% highest value compressive strength. More than all the ingredients replaced with fly ash and Meta kaolin. When considering the flexural strength of replacement cement with 10% by Meta kaolin the maximum flexural strength of 80 ksc was higher than that of control concrete and all other ingradient. Experimental tensile strength at 28 days result found that replacement cement by fly ash at 35% gave the highest tensile strength of 28 ksc and gave higher tensile strength than all other ingradient. From the impact strength test at age 28 days it was found that the replacement cement 35% by fly ash gave the highest impact strength of 92.00 joule than the 20% and 50% respectively and higher impact strength than that of all kaolin. Except for control concrete.

This objective research to study the possibility of used pozzolan material in the ternary blend by fly ash metakaolin and silica powder by replacement cement partially on the strength and resistance to chloride migration. Consideration of concrete with compressive strength in the range of 240-350 kg per sq. cm by varying the ratio of water/binder (w/b) there are three values are 0.4 0.45 and 0.50 and variable amounts of replacement cement some. The ternary blend of the fly ash metakaolin and silica powder of percentage of 0 2.5 5 10 15 20 and 25 by weight of cement. and the control specimens (w/b) without contain fly ash kaolin and silica powder the slump test in the range of 3-5 cm and the use superplasticizer to control the slump test of concrete. By casting specimens of cylindrical diameter 10x20 cm cube 10x10x10 cm and the beam size 10x10x35 cm after curing 28 days and test compressive tensile and flexural strength of concrete all specimens each ingredient by Chloride Migration Test method and the results showed that concrete is a mixture with pozzolan such as silica powder metakaolin and fly ash with amount increase replacement. The increase will help improve the quality of the concrete physical properties. The increased of compressive and Tension strength as the percentage increase especially to replacement cement increased by fly ash metakaolin and silica powder reduces the penetration of chloride in concrete respectively As a result of the porosity of the concrete with lower amounts of tightness concrete has increased

This research aims to study the possibility of steel fibers plastic fiber (polypropylene) fly ash and metakaolin mixed into the concrete. The concrete used in the research of the w / c 0.42 By 0.5 percent in the volume of steel fiber and poly propylene fiber in the amount of 0.25 percent by weight of the concrete. Concrete example of this test consisted of plain concrete(OPC).Concrete mixing materials pozzolan fly ash mixed plastics synthetic fibers of the type poly propylene fiber(FA/PP)concrete mixing materials pozzolan fly ash mixed plastics synthetic fibers of the type steel fibers (FA/ST) concrete mixing materials pozzolan meta kaolin mixed plastics synthetic fibers of kind polypropylene fiber(MK/PP) and concrete mixing materials pozzolan meta kaolin mixed plastics synthetic fibers of the typesteel fibers (MK/ST) by casting a cylindrical sample size 10 x 20 cm. Sample size 10x10x10 cm. cube and sample size 10x10x35 cm. beam. After 28 days and cure water concrete examples to test the strength of the pull compressive strength and flexural strength. And to test the movement of chloride through the concrete with Chloride Migration Test. Then bring the strength of the pull compressive strength flexural strength and the chloride permeability of concrete. Bringing concrete materials pozzolan mixed with synthetic fibers to develop the quality of concrete with improved efficiency and also reduces the porosity of the concrete. And permeability of chloride formed in the concrete (Only in landscape with the sea). The test can tell. Concrete mixing materials pozzolan with synthetic fibers to make a significant impact on the properties of concrete is improved as well. Depending on the type of polyester and the amount of material to pozzolan blended.