The objective of this research was to study the antibacterial activity of 16 samples of indigo dyed fabrics that are produced and sold in Sakon Nakhon Province. Effect of moisture and pH of indigo dyed fabrics on bacterial growth were also determined. The result of the study shows inhibition of S. aureus TISTR 746 and E. coli TISTR 073 by agar diffusion plate test all samples could inhibit Saureus TISTR 746 (accounted as 100%) and only 9 samples could inhibit E. coli TISTR 073 (accounted as 56.25%). Whereas the study of antibacterial activity by AATCC test method 100-2004 at 24 hours was found that the natural indigo dyed fabrics code A3-1 could inhibit both bacterial strains in the highest level. The result also shows the effect of moisture and pH of indigo dyed fabrics on bacterial growth it was found that the increased humidity levels of indigo dyed fabrics have effect on the reduction of the inhibition efficacy of both strains. While indigo dyed fabric with pH 3.0 was found to inhibit most of the growth of both strains. In addition images obtained using a scanning electron microscope (SEM) could clearly confirm the property of indigo dyed fabric on inhibition of S. Aureus TISTR 746 and E. coli TISTR 073.

The objective of this study is to explore a method to improve UV protection and antibacterial properties of the cotton yarn surface to produce high-quality textile products. Cotton yarns were coated with sodium hydrogen phosphate magnesium chloride softener solution and 0 to 0.54 M of polyvinyl alcohol to hold surface yarns to the yarn body using the winding machine. The coated yarns were analyzed using Field emission scanning electron microscope Fourier transform infrared spectroscopy and UV-Vis spectrophotometer. Optimal results were achieved when coating with 0.45 M PVA exhibited UV protection was excellent protection. The cotton yarn coated 0.45 M polyvinyl alcohol displayed the antibacterial activity in the presence of Staphylococcus aureus and Escherichia coli was 87 and 91% respectively. The expected overall properties may open the way towards new applications of high performance fabrics leading to an innovative product development in the textile industry