Case Study Development of Welding Machine for Sterling Silver Jewelry Parts With 500-amp electrical arc system for welding closing porous jewelry after casting. The problem can be solved by welding closing porous or by the jewelry. It is an alternative to repairing the work piece. The efficiency of electrical arc welding equipment can be repaired to a certain extent. Based on the results of the experiments the welding and repairing porous porcelain parts were rated at 500 amperes by random sampling of 4 time slots 5 seconds 10 seconds 15 seconds and 20 seconds. Examine the most appropriate porous or porous workpiece for 20 seconds with 18 complete workpieces capable of sealing or milling. A good percentage of 90 percent of the performance of an electrical arc welding machine for welding sealing or cutting.

This research is a study of the optimum heat temperature for baking sintered castings for burnout removal of EC 500 type ash wax from cast mortar. Improving jewelry casting process to reduce waste from silver jewelry production process. By studying the temperature of the mortar. To burn remove wax from the mortar and clean the gaps. Then try to bring silver water instead of metal casting. The results of a baked casing study using the EC500 housing prototype from the study showed that the EC500 wax material is melted from all solids to ash wax by heating at 850 ° C to burn. Remove ash wax which makes the cavity clean. When the casting was casted with 925 sterling silver the most complete workpiece after the improvement of the waste jewelry casting process was found to be 1 piece 1 percent 99 pieces or 99 percent.

The purpose of this research was to investigate the optimum heat temperature for the EC500 wax cured basecoat extrusion from all castings without waxing in the mortar. To reduce waste when the casting mortar through the casting process Silver Sterling 925 silver jewelry company Muang District Chiang Mai where the waste is caused by waxing outflow. The imperfections and leave waxing inside. Experiment with high temperature heat in mortar. And analyze the quality of work surface after casting with microscope. To find defects such as droplets and porosities caused by a range of temperatures. Temperature of baking mortar There is a difference from the conventional waxing mortar temperature. That is outflow of EC500 type wax. In the mortar to live. High heat The results of the 100 sample EC500 wax samples were tested at a temperature of 25 ° C. The mortar temperature was 700 ° C. 60 percent of waste was found the mortar was laid at 750 ° C 54 percent of waste was found. The mortar temperature was 800 ° C 32 percent waste was found the mortar temperature was 850° C Detecting 1 percent waste. The results of the study show that heat temperatures of up to 850 ° C can solve the problem of casting sterling silver alloys from the EC500 wax model. Finds the least waste.

โครงการทำเครื่องประดับเงินลวดลายโบราณ ชื่อวิชา ออกแบบเครื่องประดับ / การทำต้นแบบเครื่องประดับ ผู้สืบทอด อาจารย์จักรกฤษณ์ ยิ้มแฉ่ง กำหนดการ วันอังคารที่ 21 กรกฎาคม พ.ศ. 2558 เวลา 9.00 – 16.00 น. สถานที่ สาขาเทคโนโลยีแม่พิมพ์เครื่องประดับ คณะวิศวกรรมศาสตร์ มทร.พระนคร จำนวนนักศึกษา 12 ราย วัตถุประสงค์ของโครงการ มีดังนี้ 1. เพื่อให้นักศึกษามีความเข้าใจเรื่องเทคนิคการทำเครื่องประดับเงินลวดลายโบราณ 2.เพื่อให้นักศึกษาสามารถนความรู้ด้านเทคนิคงานช่าง ไปประยุกต์ใช้ในการออกแบบเครื่องประดับ 3. เพื่อให้นักศึกษามีแนวคิดเพิ่มเติมในการบูรณาการความรู้ 4.เพื่อให้นักศึกษาสืบทอดภูมิปัญญาศิลปวัฒนธรรมทางช่างการทำเครื่องประดับลวดลายโบราณ 5. เพื่อเป็นโครงการในการบูรณาการการเรียนการสอน รายละเอียดการถ่ายทอด สอนตามกรรมวิธีโบราณ เช่น การหลอม การรีด การแผ่ การตีลวดลาย การดัดม้วน และการเชื่อมประสาน การวาดลงลาย การตอกลาย ผลที่คาดว่าจะได้รับ 1. นักศึกษามีความรู้ความเข้าใจในเทคนิคงานผลิตแหวนลวดลายโบราณ 2. นักศึกษาสามารถสร้างแนวคิดในการออกแบบ และหาแรงบันดาลใจในการศึกษาจากการอบรม 3. นักศึกษาสามารถประยุกต์งานช่างสิบหมู่ มาสร้างงานออกแบบเครื่องประดับได้ 4. ผู้เข้ารับการอบรมมีความตระหนักในความรับผิดชอบต่อการอนุรักษ์ศิลปช่างสิบหมู่