This research is aimed at studying the development of strong and high strength fiberboard from coconut fiber and corn plant. This is the second consecutive year by using natural latex. To enhance thermal insulation performance. By using the cement ratio: fine sand: coconut pulp: corn fiber: water: surfactant: surfactant is 1: 0.2: 0.0125: 0.0375: 0.3: 0.03: 0.04 by weight Then add natural rubber latex at cement ratio: 5: 1 ratio of natural rubber latex: 1: 0.05 1: 0.10 1: 0.15 1: 0.20 and 1: 0.25 by weight tested in accordance with TIS 878- 2537 on cement slabs. : High density the test results show that the ratio of 1: 0.05 is the fiber cement ratio. The most appropriate the amount of natural latex said. Can make fiber Cement sheets. Best compression and bending strength. And has passed the standard TIS 878-2537 cement fiberboard developed this can help reduce the amount of natural latex is very high. And have a good thermal insulation properties

This research aims to study the application of coconut meal and corncob fiber as high density cement-bonded fiberboard. The cement: fine sand: coconut meal and corncob fiber: water: cement setting accelerator (aluminium sulphate (Al2(SO4)3) calcium chloride (CaCl2) sodium silicate (Na2SiO3)) ratio is equal to 1: 0.2: 0.05: 0.3: 0.03 by weight. The fibers are taken from coconut meal: corncob that 5 ratios are used following: 0.0500: 0 (CN0) 0.0375: 0.0125 (CN25) 0.0250: 0.0250 (CN50) 0.0125: 0.0375 (CN75) and 0: 0.0500 (CN100) by weight. 12% of Sodium Hydroxide (NaOH) was used to modify the fibers by using 1: 10 of fiber: solution and boiling 100 degree of Celsius (1-3 hours). The fiberboard production use pressure casting in normal temperature (30 – 35 degree of Celsius) and 0.75 g/cm3 of density. Resulting the CN75 ratio is suitable ratio which pass TIS 878-2537 standard (cement bonded particle board: high density) and has good physical properties mechanical properties and thermal insulation. The most suitable cement setting accelerator is calcium chloride (CaCl2).

This research aims to study the application of coconut meal and corncob fiber as high density cement-bonded fiberboard. The cement: fine sand: coconut meal and corncob fiber: water ratio is equal to 1: 0.2: 0.05: 0.3. The fibers are taken from coconut meal and corncob that 5 ratios are used to all of fiber mixing. The fiberboard production use casting in normal temperature. Resulting the CN75 ratio (coconut meal and corncob fiber is equal to 0.0125: 0.0375) is suitable ratio which pass TIS 878- 2537 standard (cement bonded particle board) and has good physicalproperties mechanical properties and thermal insulation.

This research aims to study the water hyacinth fiber inside high density cement fiber board. By using ratio components among cement : fine sand : water hyacinth fiber : water : catalyst accelerated the formations of cement (aluminum sulfate (AI2 (SO4) 3) calcium chloride (CaCl2) sodium silicate (Na2SiO3)) on the ratio 1: 0.2: 0.075: 0.3: 0.03 by weight of total water hyacinth fiber. The 5 ratios consist of 0.0 (A1 D1 formulae) 0.025 (A2 B2 C2 D2 formulae) 0.050 0.03 (A4 B4 C4 D4 formulae) and 0.1 (A5 B5 C5 D5 formulae) by weighted all fibers were treated with sodium hydroxide solution (NaOH) at a concentration of 12%. The fiber to solution ratio was 1: 10 boiled in open system at 100 °C for 1 - 3 hours. By compressing the mixture cast machine at normal temperature (30 - 35 °C). Use a density of 0.75 g / cm3. From the test results the ratio B4 is the appropriate ratio. Can pass TIS 878- 2537 Cement Board: high density and physical properties mechanical properties and thermal insulation are good. Accelerate the formation of the most suitable cement is calcium chloride (CaCl2)

This research aims to study the using oil palm fiber to develop cement-bonded fiberboard product. The mixture ratios of Portland cement type1: fine sand: oil palm fiber:tap water: catalyst are 1 : 1.95 : 0.05 : 0.40 : 0.03 1 : 1.94 : 0.06 : 0.40 : 0.03 1 : 1.93 : 0.07 : 0.40 : 0.03 1 : 1.92 : 0.08 : 0.40 : 0.03 and 1 : 1.91 : 0.09 : 0.40 : 0.03 by weight. The cement-bonded fiberboard samples are cast in 30 x 30 x 1.5 centimeter in dimension. The cement-bonded fiberboard sample testing follows the TIS 878-2537. The results show that the density thermal conductivity bending strength modulus of elasticity and tension perpendicular to surface of cement-bonded fiberboard with high quantity of oil palm fiber are lower than cement-bonded fiberboard with low quantity of oil palm fiber while that the water absorption and swelling in water of cement-bonded fiberboard with high quantity of oil palm fiber are higher. However all of oil palm fiber samples with lower than 0.06 of ratio can pass the standard.