This Research is to Study the Development of 6k White Gold Low Alloys Metal for Jewelry Production The Optimum Conditions for Casting Jewelry and Jewelry were Investigated. The Results of the Experiments Show that the Chemical Composition of the 8k White Gold Low Alloys is Slightly Different when Compared with XRF (X-ray Fluorescence Spectrometers) Pre-and Post-Melting Quantities The Heat of the Test Specimen was found to be 33.33%Au+50.67%Ag+10%Cu+5%Zn+1%Sn33.33%Au+50.67% Ag+8% Cu+7%Zn+1%Sn and 33.33%Au+50.67%Ag+8%Cu+8%Zn+0%Sn It is Found that the Heat from the Beginning to the Level of Change before the Liquid is used the Average Temperature of 458.9 – 326.3 Degrees Celsius Respectively 33.33%Au+50.67%Ag+8%Cu+7%Zn+1%Sn It is the Formula that Gives the Lowest Value of Liquid State Change from 326.3 Degrees Celsius to the Best Value of this Experiment. Suitable for use in the Manufacture of Jewelry due to its Melting Ability for Molding. Melting for Molding and Formed by Hand. The Amount of Zinc(Zn) may be an Important Factor in the Variation which is Directly Proportional to the Maximum Increase in the Final order of 7 Percent

This Research is to Study the Development of 6k White Gold Alloys for Jewelry Production. By Studying the Influence of 6k White Gold Alloys on Physical Properties for Jewelry Molding Process. Of 6k Gold Alloys at Various Compound Rates. The Results of the Experiments Show that the Chemical Composition of 6k White Gold Alloys is Slightly Different when Compared with the XRF (X-ray Fluorescence Spectrometers). Compare the pre and Post-Melting Quantities. The Result of the Compounding Test with the Color Level of 6k White Gold at the Compound Rate 25%Au+54%Ag+0%Cu+3%Zn+18%Pd The Lowest Color Level was L * = 82.14 a * = -0.16 b * = 7.71 and the Lowest Color Difference was 21.07. With other Ingredients It Shows that the Test Specimen of 6k White Gold has a Rather Greenish Color and is Slightly Yellowish Compared to the Blue Line that Approaches the Standard line. These Properties are the Physical Properties Required to Produce a 6k White Gold Jewelry Body.

This Research is to Study the Development of 6k White Gold Alloys for Jewelry Production.The Optimum Conditions for Casting Jewelry and Jewelry were Investigated. The Results of the Experiments Show that the Chemical Composition of the 6k White Gold Alloys is Slightly Different when Compared with XRF (X-ray Fluorescence Spectrometers) Pre-and Post-Melting Quantities The Heat of the Test Specimen was found to be 5%Au+42%Ag+12%Cu+3%Zn+18%Pd 25%Au+46%Ag+8%Cu+3%Zn+ 18%Pd 25%Au+50%Ag+4% Cu+3% Zn+18% Pd and 25%Au+54%Ag+0%Cu+3%Zn+ 18%Pd It is Found that the Heat from the Beginning to the Level of Change before the Liquid is used the Average Temperature of 702.3 - 636.7 Degrees Celsius Respectively 25%Au+54%Ag+0%Cu+3%Zn+18%Pd It is the Formula that Gives the Lowest Value of Liquid State Change from 636.7 Degrees Celsius to the Best Value of this Experiment. Suitable for use in the Manufacture of Jewelry due to its Melting Ability for Molding. Melting for Molding and Formed by Hand. The Amount of Zinc(Zn) may be an Important Factor in the Variation which is Directly Proportional to the Maximum Increase in the Final order of 3.58 Percent.

This Research is to Study the Development of 6k White Gold Alloys for Jewelry Production. The Influence of Admixtures on Mechanical Properties was Investigated (Tensile Strength and Hardness) of 6k White Gold Alloys at Various Composite Ratios. The Results of the Experiments Show that the Chemical Composition of 6k White Gold Alloys is Slightly Different when Compared with the XRF (X-ray Fluorescence Spectrometers). Compare the pre and Post-Melting Quantities. Test results of Mechanical Properties of Test Pieces. The Tensile Strength of the 6k Gold Alloy is 25% Au+46%Ag+8%Cu+3%Zn+18%Pd The Highest Value was 1.14 kN / mm2 the Lowest Percentage was 64% and the Hardness was 259.87HV. The Result of this Test is that the Mechanical Properties of the Material are Brittle Material. When the Mold is Formed the Fracture and Forming will be Difficult. 25%Au+42%Ag+12%Cu+3%Zn+ 18%Pd 25%Au+50%Ag+4%Cu+3%Zn+18%Pd and 25%Au+54%Ag+0%Cu+3%Zn+ 18%Pd Tensile Strength in the Range of 0.66-0.70 kN / mm2 Percentage of Elongation in the Range of 84-90% and Hardness of 277.60 244.60 and 186.73HV Respectively. The Mechanics will Show that the Alloys of White Gold 6k 25%Au+54%Ag+0%Cu+3% Zn+18%Pd Have Similar Tensile Strength. The Maximum Percentage of Elongation is 90% and the Minimum Hardness is 186.73HV. It is Suitable for Forming because it has Ductile Material. This is a Good Mechanical Property in the Metal Forming Machine.

This Research is a Development of 8k White Gold low Alloy Metal Components for Jewelry Pieces. By Study and Analyze the Influence of Silver Alloy Gold Alloy Bronze Alloy Zinc Alloy and Tin Alloy. Which Affect Microstructure and Mechanical Properties. (The Different of Color Scales) And Resistance Behavior of Lowered 8k White Gold Alloy in Varies Ratio. The Results Showed that Tests and Analysis to Find the Quantities of Elements has found out that Chemical Components of 8k White Gold Low Alloy Metal had a Little Different Quantities when Compared Between Before and After Centrifugal Casting Process. The Tests and Analysis Results of Mechanical Properties of Test Pieces Showed that the Hardness and Tensile Strength of 8k White Gold Low Alloy Metal with Mixture of 33.33%Au+50.67%Ag+10%Cu+5%Zn+1%Sn had Minimum Ultimate Tensile Strength Equal 0.54 kN/mm2 Minimum Elongation Percentage of 55% and Maximum Hardness of 137.0 HV. The Test Results also Show that the Mechanical Properties of the Material are Brittle Material. When Perform a Forming Process the Pieces will be Easily Broken which was Meant that the Forming Process would be Difficult. But The Color Level of the Test Pieces at this Composite Ratio had the Best Metal Color Level. The Brightness L * = 74.87 was a * = -0.89 b * = 13.74 and the Value of ΔE with the Lowest Color Difference Level of 1.35. Compared to other Varies Ratio. It Showed that 8k White Gold Low Alloy Metal Test Pieces were Very Green and Came out Slightly Yellow Compared to the Blue Line that Approached the Standard Line. These Properties were the Physical Properties Required in 8k White Gold Low Alloy Metal Jewelry Pieces Production. Also there were the Results of 8k White Gold Low Alloy Metal in Two Formulas 8k 33.33%Au+50.67%Ag +8%Cu+7%Zn+1%Sn 33.33%Au+50.67%Ag+8%Cu+8%Zn+0%Sn. These Formulas had Tensile Strength in the Range of 1.10 0.60 kN /mm2 Elongation Percentage in the Range of 70 61% and Hardness of 115.6 123.3HV Respectively. The Results of the Mechanical Properties Test of the Test Pieces Showed that 8k White Gold Low Alloy Metal 33.33% Au+50.67%Ag+8%Cu+7%Zn+1%Sn has Similar Tensile Strength but Maximum Elongation Percentage of 70% and Minimum Hardness of 115.6HV. Which was Suitable for Forming Because of good Ductility and Stretchness Properties (Ductile Material). Forming would be Easy. These were Good Mechanical Properties for Forming Precious Metals.