Springback behavior is a major problem of sheet metal forming process. Especially aluminum alloy which often encounter such problems often. At present aluminum alloy is increasingly of used in the automotive industry for replace of the steels due to its lightweight and good finished surface. This work aims study to springback behavior of cold rolled aluminum alloy (AA6016) during air-bending process by ISO7438/2010 test standard. To analyze the influence of bending process parameter are included: sheet thickness punch radius bending angle die open and the ratio of bending radius and material thickness (r/t) effecting to springback behavior. The results are clearly that the springback angle is likely to increase with increase of the punch radius size of die open and the ratio of punch radius and sheet thickness and the springback tenor to decrease when the sheets thickness and bending angle increased. The increased bending angle will resulted to bending surface region is roughness increase and crack occurred to follow. As a result the bending force and the springback angle decreased.

This paper discusses the mixed alloy silver pink by spending innocent Alloy capital ratio of 58.00% and check the analysis of color against Silver 925 under the metal content of about 58.40% alloy 41.60% result. According to the study the researchers used to hold above ingredients prototype to develop a mixture of silver to feature pink by analyzing the color (Color Analysis) tested the color of silver mixed pink capital ratio of 116.80 alloy. 83.20 wt.% has a shiny bright color space the L 67.17 a = 9.60 b = 2.04 a compound that can be used to produce silver mixed pink. In the manufacturing industry has for the user.