The study of silver metal used in the non-plated jewelry industry was found to be dull or black but it was a basic feature of silver. To react with air easily in Thailand. The hot weather must be maintained regularly. The concept that we can study the development of silver metal with resistance to tarnish to slow down will have a positive effect on the jewelry industry. The team has developed a concept to bring other elements to meet the potential. The element used here is palladium (Pd) because the palladium is in the same group as the nickel and platinum groups in the periodic table. It is a metal (Nobel Metal) which is very durable corrosion. Usually white is natural and when used to polish the skin is glistening and in most cases in the jewelry industry is often used as part of the alloy such as making the natural gold color close to the platinum. The authors performed the experiments by introducing silver metal with palladium in an appropriate ratio and tested it with artificial stone. And save the record. It is divided into 4 periods of 5-20 days in normal temperature. The results of the study showed that 92.5% copper 6.8% and 0.7% palladium had a shade of L value of 59% over 20 days. It can be used to produce silver jewelry at a lower tarnished rate. In the jewelry industry

The results of the experiments were found that the temperature of the castings was higher than that of the silver alloys. The workpiece temperature is 500C the workpiece is good 26%. The workpiece is 74%. The temperature is 550C. The workpiece is 26%. The workpiece is 74%. The temperature is 600C. The workpiece is 40%. The workpiece is 60%. The workpiece is a fin. There are many factors that cause fins on the workpiece. Use of low-strength mortar In addition the use of excessive compression or heat transfer resulting in the expansion and shrinkage is not equal. This causes the cracking of the metal water to expand at a temperature of 650 ° C. The fine specimen 56% of the workpiece loses 44%. This temperature results in the smallest workpiece caused by the uneven surface. Cause of the cooling rate in each part of the casting is not equal. And at 700 degrees Celsius it is best to cast silver ornaments with pink color because the results show that the work is minimal. There are 70% good work piece 30%

This Research is a Development of 8k White Gold low Alloy Metal Components for Jewelry Pieces. By Study and Analyze the Influence of Silver Alloy Gold Alloy Bronze Alloy Zinc Alloy and Tin Alloy. Which Affect Microstructure and Mechanical Properties. (The Different of Color Scales) And Resistance Behavior of Lowered 8k White Gold Alloy in Varies Ratio. The Results Showed that Tests and Analysis to Find the Quantities of Elements has found out that Chemical Components of 8k White Gold Low Alloy Metal had a Little Different Quantities when Compared Between Before and After Centrifugal Casting Process. The Tests and Analysis Results of Mechanical Properties of Test Pieces Showed that the Hardness and Tensile Strength of 8k White Gold Low Alloy Metal with Mixture of 33.33%Au+50.67%Ag+10%Cu+5%Zn+1%Sn had Minimum Ultimate Tensile Strength Equal 0.54 kN/mm2 Minimum Elongation Percentage of 55% and Maximum Hardness of 137.0 HV. The Test Results also Show that the Mechanical Properties of the Material are Brittle Material. When Perform a Forming Process the Pieces will be Easily Broken which was Meant that the Forming Process would be Difficult. But The Color Level of the Test Pieces at this Composite Ratio had the Best Metal Color Level. The Brightness L * = 74.87 was a * = -0.89 b * = 13.74 and the Value of ΔE with the Lowest Color Difference Level of 1.35. Compared to other Varies Ratio. It Showed that 8k White Gold Low Alloy Metal Test Pieces were Very Green and Came out Slightly Yellow Compared to the Blue Line that Approached the Standard Line. These Properties were the Physical Properties Required in 8k White Gold Low Alloy Metal Jewelry Pieces Production. Also there were the Results of 8k White Gold Low Alloy Metal in Two Formulas 8k 33.33%Au+50.67%Ag +8%Cu+7%Zn+1%Sn 33.33%Au+50.67%Ag+8%Cu+8%Zn+0%Sn. These Formulas had Tensile Strength in the Range of 1.10 0.60 kN /mm2 Elongation Percentage in the Range of 70 61% and Hardness of 115.6 123.3HV Respectively. The Results of the Mechanical Properties Test of the Test Pieces Showed that 8k White Gold Low Alloy Metal 33.33% Au+50.67%Ag+8%Cu+7%Zn+1%Sn has Similar Tensile Strength but Maximum Elongation Percentage of 70% and Minimum Hardness of 115.6HV. Which was Suitable for Forming Because of good Ductility and Stretchness Properties (Ductile Material). Forming would be Easy. These were Good Mechanical Properties for Forming Precious Metals.

This paper discusses the mixed alloy silver pink by spending innocent Alloy capital ratio of 58.00% and check the analysis of color against Silver 925 under the metal content of about 58.40% alloy 41.60% result. According to the study the researchers used to hold above ingredients prototype to develop a mixture of silver to feature pink by analyzing the color (Color Analysis) tested the color of silver mixed pink capital ratio of 116.80 alloy. 83.20 wt.% has a shiny bright color space the L 67.17 a = 9.60 b = 2.04 a compound that can be used to produce silver mixed pink. In the manufacturing industry has for the user.

การวิจัยนี้เป็นการศึกษาพฤติกรรมการอบชุบด้วยกระบวนการทางความร้อนของโลหะเงิน เจือต่ำ58.45wt%Ag +41.55wt%Cu โดยทำการเปรียบเทียบกับสมบัติของโลหะเงินสเตอร์ลิง 925 และโลหะเงินเจือต่ำ 58.33% เพื่อศึกษาสภาวะที่เหมาะในหาการปรับปรุงคุณสมบัติเชิงกลและโครงสร้าง จุลภาคของโลหะเงินเจือต่ำที่เป็นไปตามมาตรฐานผลิตเครื่องประดับ ผลจากการศึกษาโลหะเงิน 58.33 % ที่อัตราส่วนผสม 58.33Ag+36.66Cu+5.01Sn ซึ่งมี ค่าคุณสมบัติเชิงกลจากการทดสอบเบื้องต้นมีค่าเหมาะสมที่สุด จากนั้นท่าการศึกษาค่าความแข็งแรงดึง สูงสุดแบบเส้นลวดพบว่ามีค่าความต้านทานแรงดึงสูงสุดเท่ากับ 0.36 MPa ค่าเปอร์เซ็นต์การยืดตัว 0.11% เมื่อท่าการอบที่อุณหภูมิ 650 °C เวลาในการอบ 10 นาที ซึ่งปล่อยให้ชิ้นงานเย็นตัวในอากาศที่ อุณหภูมิห้องปกติ และค่าความแข็งจากการทดสอบมีค่าสูงสุดเท่ากับ 105.12 HV อบที่อุณหภูมิ 600 °C เวลาในการอบ 10 นาที ซึ่งปล่อยให้ชิ้นงานเย็นตัวในอากาศที่อุณหภูมิห้องปกติ ศึกษาโครงสร้างจุลภาค ของโลหะเงินเจือต่ำ 58.33Ag+41.57Cu+0.10Sn เมื่อท่าการอบปรับปรุงคุณสมบัติทางความร้อนและการ ชุบแข็งแบต่างๆ พบว่าโครงสร้างจุลภาคของชิ้นงานทดสอบหลังปล่อยให้เย็นตัวในอากาศ เกิดการ เปลี่ยนแปลงจาก β phase ที่มีขนาดเล็กลงเป็นโครงสร้าง Eutectic phase ที่มี α -phase และ β - phase ขนาดเล็กและละเอียด ซึ่งมีลักษณะสอดคล้องกับโครงสร้างจุลภาคของเฟสไดอะแกรมสมดุลโลหะ เงิน-ทองแดง ผลจากการทดลองและวิเคราะห์หาค่าคุณสมบัติเชิงกลของชิ้นงานทดสอบและโครงสร้างจุลภาค ที่ได้จากการทดลองในสภาวะต่างๆ มีค่าที่เป็นไปตามมาตรฐานของเครื่องประดับเงินตามมาตรฐาน อุตสาหกรรมการผลิตเครื่องประดับ ทั้งของในประเทศและต่างประเทศ