This research study analyzes the problem of waste water from the burning of palm trees which are used as fuel for power generation of palm ash. It is used to ferment biogas as a fuel for power generation where a large amount of wastewater from the gas digester is completed. The wastewater is then pumped out of the gas digester. Biological in large quantities Therefore to study the analysis of wastewater to find a method for designing a wastewater treatment system from high voltage systems from the corona discharge principle when adding ozone it is necessary to analyze the chemical effects of the wastewater according to the standard values of the Department of Industrial Works.

The results of the study on the optimum temperature for baking soda extinguishers were investigated. B9R-3-EMERALD Using brass material in experiments. It was found that the temperature of 750˚C was good for 48% of the workpiece 52% was found that the workpiece was damaged at the surface of the work very porous at the surface. Caused by the heat of metal water pouring into contact with the moisture of the mold resulting in gas. High temperature of metal water Or eliminate gas in metal water is not exhausted. The workpiece is not suitable at a temperature of 800 ° C with a good workpiece of 76%. The workpiece loses 24%. The workpiece loses less punch at the lower porosity as well at 750˚C in temperature. 850˚C workpiece 96% workpiece 4% workpiece the workpiece is almost out. It is less than 750˚C and 800˚C at porosity. And at 900˚C the workpiece is 100% of the workpiece 0%. The workpiece is the best. Workpiece waste from the minimum. The test results make the temperature at 900 ° C is the cleanest casing temperature

The purpose of this research was to study the temperature of burning surf clam shell for soil quality improvement. The experiment was divided two parts 1) the study of the optimum temperature for calcium oxide production by burning 800 900 1000 and 1100 °C 2) the study of using calcium oxide to improve soil qualities of acidic soil and saline soil. The parameters used in the analysis included elements of soil particles soil moisture pH conductivity total content nitrogen phosphorus and potassium. The results showed that the optimum temperature for the production of calcium oxide was 1100 °C since it provided the highest calcium oxide content of 90 % by weight. After applying calcium oxide into acidic soil the composition of soil particles was changed from sandy clay to sandy clay loam. In contrast the soil particle was not changed but the proportion was changed in saline soil. It was also found that calcium oxide reduced soil moisture and influenced the acidity of soil by increasing the pH from 3.39 to 6.92 in acidic soil and 6.49 to 9.11 in saline soil. In addition it was found that the electrical conductivity of the soil was related to salinity. In acidic soil the conductivity of before and after inputting calcium oxide were 0.87 and 1.24 dS/m respectively. In the case of saline soil the conductivity of before and after improvement were 14.37 and 18.80 dS/m respectively. Besides it was found that the total content of nitrogen phosphorus and potassium were reduced after the experiment.

The research aims to investigate the possibilities of crushed oyster shell (OS) not have to go through the process of burning as a substitution cement for concrete blocks. The cement was replaced with crushed oyster shell not process burning (OS) at 0% 10203040 and 50% by the weight of the binder. After that the concrete blocks were tested to determine the compressive strength and moisture absorbed of the concrete blocks cured for 7 142856 and 90 days The result showed that the compressive strength of the concrete blocks which replaced cement with OS (at the proportion of 10% by the weight of the binder) at 28 days had the compressive strength and water absorbed accordance with the TIS 58-2533 on non-load bearing concrete blocks.Moreover the concrete blocks which replaced cement with OS at the proportion of 20 % and 30 % had the compressive strength equivalent to 28 days compressive strength of TIS 58-2533 standard at 56 and 90 days respectively and decreased when the percentage in addition to OS in concrete blocks of 40 and 50 %. Tested results also showed that the water absorbed of concrete blocks increased when the percentage of replacement of OS in binder increased at 10 20 30 40 and 50%. The economical of concrete blocks it has manufactured unit cost is 2.60 baht. Whereas the concrete block containing crushed oyster shell at 10-30% it has manufactured unit cost at 2.12-2.44 baht respectively.

The pomelo peels charcoal was successfully prepared by traditional charcoal burning and its adsorption of methylene blue was investigated. The influences of methylene blue adsorption including contact time and methylene blue initial concentration were studied at room temperature. The adsorption rate initially increased rapidly until 24 h and 600 mg/L of methylene blue initial concentration. The further increase in contact time and methylene blue initial concentration did not significantly increase the adsorption due to it reached equilibrium. Kinetic of adsorption were investigated that the pseudo-second order model best described adsorption kinetic data. The adsorption isotherms were evaluated and the data correlated with Langmuir adsorption model with the maximum adsorption capacity was found to be 166.67 mg/g. The adsorption of pomelo peel charcoal was studied comparing to other adsorbents at the same experimental conditions. The results showed higher adsorption of pomelo peel charcoal than dried pomelo peel longan wood charcoal coconut shell charcoal litchi wood charcoal and tamarind wood charcoal respectively.