In this research scaffolds of β-tricalcium phosphate (β-TCP) and zinc nickel ferrite (ZnxNi1-xFe2O4) were simply fabricated via the uniaxial pressing together with pressureless sintering which can be tailored for specific applications. The morphology of ZnxNi1-xFe2O4/β-TCP scaffolds with all formulas obtained from the SEM result revealed the larger grains the higher porosity and higher interconnectivity with increasing of ZnxNi1-xFe2O4 amount in β-TCP matrix. The high porous structure of the composite scaffold provided high surface area for cell attachment indicative of good cell growth and differentiation. Biological in vitro test using direct contact method with human cells revealed that the composite scaffold of β-TCP and Zn0.8Ni0.2Fe2O4 with all ratios induced the higher growth of Human osteoblast cells and the better cell spreading on surface of specimens

In this work fiber mat based on silk sericin and thunbergia laurifolia linn extract was developed via electrospinning technique for wound dressing application. The waste cocoons were selected from Nakhon Ratchasima 1 (K1) with appropriate spicy for extracting the silk sericin protein. Trunk of thunbergia laurifolia linn was selected for preparing thunbergia laurifolia linn extract. Polyvinyl alcohol (PVA) with several concentrations were chose and fabricated to fibers by electrospinning technique to investigate suitable polymer concentration for mixing silk sericin and thunbergia laurifolia linn extract. The result revealed that PVA of 9 wt % was suitable due to Several parameters were investigated to prepare the electrospun fiber of silk sericin and thunbergia laurifolia linn extract such as their mixing ratio voltage the distance between the needle and the substrate and the needle size. The results indicated that mixing ratio of silk sericin and thunbergia laurifolia linn extract at 50:50 (w/w) voltage of 15 kV the distance of the needle and the substrate at 8 cm and the needle size of 18 were optimum condition for the fabrication of electrospun fiber with diameter of 100-200 nm and that with smooth and continue feature.