The study of silver metal used in the non-plated jewelry industry was found to be dull or black but it was a basic feature of silver. To react with air easily in Thailand. The hot weather must be maintained regularly. The concept that we can study the development of silver metal with resistance to tarnish to slow down will have a positive effect on the jewelry industry. The team has developed a concept to bring other elements to meet the potential. The element used here is palladium (Pd) because the palladium is in the same group as the nickel and platinum groups in the periodic table. It is a metal (Nobel Metal) which is very durable corrosion. Usually white is natural and when used to polish the skin is glistening and in most cases in the jewelry industry is often used as part of the alloy such as making the natural gold color close to the platinum. The authors performed the experiments by introducing silver metal with palladium in an appropriate ratio and tested it with artificial stone. And save the record. It is divided into 4 periods of 5-20 days in normal temperature. The results of the study showed that 92.5% copper 6.8% and 0.7% palladium had a shade of L value of 59% over 20 days. It can be used to produce silver jewelry at a lower tarnished rate. In the jewelry industry

The results of the experiments were found that the temperature of the castings was higher than that of the silver alloys. The workpiece temperature is 500C the workpiece is good 26%. The workpiece is 74%. The temperature is 550C. The workpiece is 26%. The workpiece is 74%. The temperature is 600C. The workpiece is 40%. The workpiece is 60%. The workpiece is a fin. There are many factors that cause fins on the workpiece. Use of low-strength mortar In addition the use of excessive compression or heat transfer resulting in the expansion and shrinkage is not equal. This causes the cracking of the metal water to expand at a temperature of 650 ° C. The fine specimen 56% of the workpiece loses 44%. This temperature results in the smallest workpiece caused by the uneven surface. Cause of the cooling rate in each part of the casting is not equal. And at 700 degrees Celsius it is best to cast silver ornaments with pink color because the results show that the work is minimal. There are 70% good work piece 30%

Case Study Development of Welding Machine for Sterling Silver Jewelry Parts With 500-amp electrical arc system for welding closing porous jewelry after casting. The problem can be solved by welding closing porous or by the jewelry. It is an alternative to repairing the work piece. The efficiency of electrical arc welding equipment can be repaired to a certain extent. Based on the results of the experiments the welding and repairing porous porcelain parts were rated at 500 amperes by random sampling of 4 time slots 5 seconds 10 seconds 15 seconds and 20 seconds. Examine the most appropriate porous or porous workpiece for 20 seconds with 18 complete workpieces capable of sealing or milling. A good percentage of 90 percent of the performance of an electrical arc welding machine for welding sealing or cutting.

The results of the study on the optimum temperature for baking soda extinguishers were investigated. B9R-3-EMERALD Using brass material in experiments. It was found that the temperature of 750˚C was good for 48% of the workpiece 52% was found that the workpiece was damaged at the surface of the work very porous at the surface. Caused by the heat of metal water pouring into contact with the moisture of the mold resulting in gas. High temperature of metal water Or eliminate gas in metal water is not exhausted. The workpiece is not suitable at a temperature of 800 ° C with a good workpiece of 76%. The workpiece loses 24%. The workpiece loses less punch at the lower porosity as well at 750˚C in temperature. 850˚C workpiece 96% workpiece 4% workpiece the workpiece is almost out. It is less than 750˚C and 800˚C at porosity. And at 900˚C the workpiece is 100% of the workpiece 0%. The workpiece is the best. Workpiece waste from the minimum. The test results make the temperature at 900 ° C is the cleanest casing temperature

This Research is to Study the Development of 6k White Gold Low Alloys Metal for Jewelry Production The Optimum Conditions for Casting Jewelry and Jewelry were Investigated. The Results of the Experiments Show that the Chemical Composition of the 8k White Gold Low Alloys is Slightly Different when Compared with XRF (X-ray Fluorescence Spectrometers) Pre-and Post-Melting Quantities The Heat of the Test Specimen was found to be 33.33%Au+50.67%Ag+10%Cu+5%Zn+1%Sn33.33%Au+50.67% Ag+8% Cu+7%Zn+1%Sn and 33.33%Au+50.67%Ag+8%Cu+8%Zn+0%Sn It is Found that the Heat from the Beginning to the Level of Change before the Liquid is used the Average Temperature of 458.9 – 326.3 Degrees Celsius Respectively 33.33%Au+50.67%Ag+8%Cu+7%Zn+1%Sn It is the Formula that Gives the Lowest Value of Liquid State Change from 326.3 Degrees Celsius to the Best Value of this Experiment. Suitable for use in the Manufacture of Jewelry due to its Melting Ability for Molding. Melting for Molding and Formed by Hand. The Amount of Zinc(Zn) may be an Important Factor in the Variation which is Directly Proportional to the Maximum Increase in the Final order of 7 Percent