This Research is to Study the Development of 6k White Gold Alloys for Jewelry Production. By Studying the Influence of 6k White Gold Alloys on Physical Properties for Jewelry Molding Process. Of 6k Gold Alloys at Various Compound Rates. The Results of the Experiments Show that the Chemical Composition of 6k White Gold Alloys is Slightly Different when Compared with the XRF (X-ray Fluorescence Spectrometers). Compare the pre and Post-Melting Quantities. The Result of the Compounding Test with the Color Level of 6k White Gold at the Compound Rate 25%Au+54%Ag+0%Cu+3%Zn+18%Pd The Lowest Color Level was L * = 82.14 a * = -0.16 b * = 7.71 and the Lowest Color Difference was 21.07. With other Ingredients It Shows that the Test Specimen of 6k White Gold has a Rather Greenish Color and is Slightly Yellowish Compared to the Blue Line that Approaches the Standard line. These Properties are the Physical Properties Required to Produce a 6k White Gold Jewelry Body.

This Research is to Study the Development of 6k White Gold Alloys for Jewelry Production.The Optimum Conditions for Casting Jewelry and Jewelry were Investigated. The Results of the Experiments Show that the Chemical Composition of the 6k White Gold Alloys is Slightly Different when Compared with XRF (X-ray Fluorescence Spectrometers) Pre-and Post-Melting Quantities The Heat of the Test Specimen was found to be 5%Au+42%Ag+12%Cu+3%Zn+18%Pd 25%Au+46%Ag+8%Cu+3%Zn+ 18%Pd 25%Au+50%Ag+4% Cu+3% Zn+18% Pd and 25%Au+54%Ag+0%Cu+3%Zn+ 18%Pd It is Found that the Heat from the Beginning to the Level of Change before the Liquid is used the Average Temperature of 702.3 - 636.7 Degrees Celsius Respectively 25%Au+54%Ag+0%Cu+3%Zn+18%Pd It is the Formula that Gives the Lowest Value of Liquid State Change from 636.7 Degrees Celsius to the Best Value of this Experiment. Suitable for use in the Manufacture of Jewelry due to its Melting Ability for Molding. Melting for Molding and Formed by Hand. The Amount of Zinc(Zn) may be an Important Factor in the Variation which is Directly Proportional to the Maximum Increase in the Final order of 3.58 Percent.