The research project investigated the effects of CoO additive on dielectric ferroelectric physical and mechanical properties of modified Bi0.5(Na0.81K0.19)0.5TiO3 ceramics were investigated. The samples were synthesized by solid state reaction technique where powders were calcined at 850 °C for 4 h and ceramics were sintered at 1050 °C for 4 h which difference heating rate controlled i.e. 100 300 and 600 °C/h for. The ceramics of BNKT/x wt.% CoO was added CoO by various x=0.00 0.10 0.20 0.30 0.60 and 0.90. Phase formation was determined by X-ray diffraction technique (XRD). The X-ray diffraction analysis of the ceramics suggests that all samples exhibited a perovskite structure. The dielectric properties under room temperature and various temperatures were also determined. Dielectric measurement data showed that the additive and heating rate controlled influenced dielectric constant and dielectric loss. Furthermore the hysteresis loop behaviors slightly changed with increasing the CoO contents.

The purpose of this project is to study the mechanical and physical properties of recycled roofing materials. The pulp extracted from the UHT beverage boxes to get aluminum foil mixed with low density polyethylene. This can be used engineering and is an option to reduce the amount of UHT boxes left over to roofing sheets. In experiment 3 aluminum foil medium size and fine then hot and extruded with 68 and 10 bar compression then cut into test pieces. To test mechanical and physical properties in accordance with the test standards: Torsion Testing Tensile strength Impact resistance Heat resistance water absorption and density testing. Compare the mechanical and physical properties of the material; different sizes of aluminum foil and compressive strength. To bring the best materials to the product. From the tests it was found that the properties of recycled composite materials From the box UHT beetroot This is made of coarse aluminum foil. 18.23 MPa bending strength 10.66 MPa tensile strength 110.987 J / m2 impact resistance 52.40 Shore-D Hardness 0.62 % Water Absorption 0.70 % Thickness Swelling 1.086 g/m3 Density 0.031 m2.K/W Thermal Resistance and 0.291 W/mK Thermal Conductivity is the best mechanical properties. Due to the large aluminum foil it can be used for high strength. Which is higher than the aluminum foil of a smaller size.