Aluminium was used in many industrial applications due to good properties such as ductile high corrosion resistant and high electrical conductivity. Since wear resistance of aluminium was very poor so that it was a limitation of using this material in several conditions. In this research aluminium was improved the wear resistance properties by using anodizing process and adding some titanium dioxide particles on the surface. The effect of anodizing process duration on the wear resistence property was studied. It was found that the process duration and amount of titanium dioxide play the important role on improvement of tribological properties of aluminium.

The purpose of this research work was to synthesize titanium dioxide supported on activated carbon and used it as a catalyst for dye decolorisation. The effect of preparing factors on titanium dioxide supported on activated carbon such as calcinations temperature and the amount of carbon supports were investigated at 300 400 and 500OC and in range of 5-30 percent by weight respectively. The X-ray diffraction (XRD) technique was used to detect the crystal structure of prepared catalysts. It was found that all peaks were anatase phase. The morphology of these catalysts was analyzed by scanning electron microscope (SEM) and transmission electron microscope (TEM) techniques. The results showed regularly distribution of titanium dioxide supported on activated carbon. The particle size of obtained catalysts was 5-10 nm. The Brunauer-Emmett-Teller (BET) technique was analyzed physical characteristic of catalysts. The specific surface area average pore diameter and pore volume of catalysts was 151.02-784.13 m2/g 26.94-64.35 and 0.24-0.55 cm3/g respectively. Furthermore the activity of obtained catalyst was carried out by using these catalysts to decolourise dye aqueous solution. The titanium dioxide supported on activated carbon 20 percent by weight can obtain 99.78% decolourisation at dye concentration 75 mg/L catalyst concentration 0.5 g/L within 90 minute. Comparison with titanium dioxide P25 (commercial grade) titanium dioxide supported on activated carbon has higher ability. This is because it was not only photocatalytic reaction but it was also absorption

This research is to study the efficiency of treating wastewater from dyeing fabric by the ozonation process. By using rutile TiO2 coated plastic media to catalyze. Which uses O3 generators with a capacity of 2.62 - 3.10 g/hr. By studying the factors that affect the treatment efficiency of COD and color such as the pH of the water used in the treatment at pH 3 pH 7 and pH 11 the initial COD concentration of 100% 50% and 25% which have values in the range of 100 -320 mg/L. O3 exposure time 120 min. From the study it is found that the efficiency of reducing the impurities in wastewater by the ozonation process in the pH 11 state the COD concentration at 50% can reduce the COD. And the maximum color is at 33.3% and 90% from the 550 ADMI color intensity with a COD of 180 mg/L. For the study of the efficiency of reducing the impurities of wastewater by ozonation process together with 2 g. of TiO2/1 L. of wastewater in the condition of pH 11 concentration COD Beginning at 100% with the ability to reduce COD values And the maximum color is at 40% and 80% of the 270 ADMI color intensity with a COD of 190 mg/L. The amount of O3 suitable for treatment has an average value of 0.0374 g/min./10.5 L. of wastewater. The duration of O3 exposure in both processes has a similar approach to the efficiency of COD and color treatment when increasing the duration of O3 exposure.