The aim of this study is developed of alkali activated high calcium fly ash to use as cementitious material to replace Portland cement. The mixture of mortar made from fly ash and sodium hydroxide solution (NaOH) was used to activate strength at concentrations of 2 4 6 and 8 molars. Superplasticizer was used to control the flow of mortar in the rage of 105 – 110. The compressive strength of mortar was determined at 7 28 45 and 60 days. The acid resistance of mortars due to sulfuric at a concentration of 3% were also investigated. The results showed the mortar made from high calcium fly ash with sodium hydroxide of 6 molar obtained the highest compressive strength which could be developed compressive strength up to 189 ksc at 60 days. For the acid resistance of mortar it was found that the of use 6 molar of NaOH activated high calcium fly ash binder had the least weight loss due to sulfuric acid attack.

This research analyzes the parameters affecting the penetrating resistance of shells on the armor surface by the finite element method. In this study the results were compared with real bulletproof armor firing tests and finite element simulations. modeling of bulletproof armor using Solid Works program. Creating and simulating armor firing pattern using ANSYS Explicit Dynamic program. damage test is based on National Institute of Justice level 3 standards with material of the ammunition is 7.62 mm tungsten carbide (WC) and speed 847 + 9.1m/s. there are two types of bulletproof armor used in this simulation 1. SKD11 2. Aluminum AL7075. The simulations is into 1 category Simulation of stacked armor plates. The sizes of the armor plates are 6 8 and 10 mm and the angles of firing of bulletproof armor are 0 30 and 45 degrees. result of this simulation armor thickness and firing angle are factors of penetration resistance. when the angle of the projectile is tilted it will cause the projectile to deflect reducing the frictional contact from the impact.

This research aims to develop the coconut coir ceiling board mixed with natural latex. The 6 ratios of gypsum plaster: coconut coir: sodium silicate: natural rubber: tap water are equal to 1: 0.15: 0.03: 0.00: 1 1: 0.15: 0.03: 0.01: 1 1: 0.15: 0.03: 0.02: 1 1: 0.15: 0.03: 0.03: 1 1: 0.15: 0.03: 0.04: 1 and 1: 0.15: 0.03: 0.05: 1 by weight. The ceiling boards were produced by casting in normal temperature (30 – 35 degree of Celsius). The properties testing of coconut coir ceiling board mixed with natural latex followed the TIS 219-2009 standard (gypsum plasterboard) including: breaking load nail pull resistance deflection water absorption density thermal conductivity coefficient and real usage. From the results 1: 0.15: 0.03: 0.03: 1 ratio is the most suitable ratio of coconut coir ceiling board mixed with natural latex. This developed ceiling boards can reduce the quantity of coconut coir waste and get the good thermal insulation ceiling board products.

The objective of this research is to develop the high corrosion resistance and good thermal insulation precast adobe wall panels mixed with natural latex. The 6 ratios of Portland cement type1: clay: rice husk ash: straw: rice husk:waterproofed liquid: natural latex: tap water were designed including: 1: 3: 0.3:0.02: 0.02: 0.02: 0: 0.4 1: 3: 0.3: 0.02: 0.02: 0.02: 0.05: 0.4 1: 3: 0.3: 0.02: 0.02: 0.02:0.1: 0.4 1: 3: 0.3: 0.02: 0.02: 0.02: 0.15: 0.4 1: 3: 0.3: 0.02: 0.02: 0.02: 0.2: 0.4 and 1:3: 0.3: 0.02: 0.02: 0.02: 0.25: 0.4 by weight. The precast adobe wall panels castedas same as the common concrete and reinforced by the bamboo. From the resultsthe proper ratio of precast adobe wall panel mixed with natural latex was 1: 3: 0.3:0.02: 0.02: 0.02: 0.1: 0.4 ratio. The properties of the proper precast adobe wall panelincluded density 1810.83 kg/m3 water absorption 17.16 % compressive strength 15.13MPa bending strength 3.01 MPa thermal conductivity coefficient 0.234 watt/m.Kelvin. Moreover the proper precast adobe wall panel mixed with natural latex also was verified by TIS.2226-2548 with properties of impact resistance deflection and hardness in medium duty (MD) level. The proper amount of natural latex effected the precast adobe wall panels to improve the mechanical properties including: increase the compressive and tensile strength decrease the density thermal conductivity coefficient and water absorption.

The objective of this research is to develop the precast adobe wall panel with high corrosion resistance and good thermal insulation. The ratio of Portland cement type1 clay rice husk ash straw rice husk waterproofed liquid and tap water was mixed and casted as same as the common concrete and reinforced by bamboo. From the results the proper prototype ratio of precast adobe wall panel was Portland cement type1: clay: rice husk ash: straw: rice husk: waterproofed liquid: tap water which equal to 1: 3: 0.3: 0.02: 0.02: 0.02: 0.4 by weight. The properties of the precast adobe wall panel prototype included density 1797 kg/m3 water absorption 16.70% bending strength 2.61 MPa compressive strength 21.40 MPa thermal conductivity coefficient 0.314 watt/m.Kelvin. Moreover the precast adobe wall panel prototype also was verified by TIS.2226-2548 with properties of impact resistance deflection and hardness in medium duty (MD) level. These straw and rice husk effected the precast adobe wall panel to decrease the density bending strength thermal conductivity coefficient and increase the compressive strength and water absorption.