This paper discusses the mixed alloy silver pink by spending innocent Alloy capital ratio of 58.00% and check the analysis of color against Silver 925 under the metal content of about 58.40% alloy 41.60% result. According to the study the researchers used to hold above ingredients prototype to develop a mixture of silver to feature pink by analyzing the color (Color Analysis) tested the color of silver mixed pink capital ratio of 116.80 alloy. 83.20 wt.% has a shiny bright color space the L 67.17 a = 9.60 b = 2.04 a compound that can be used to produce silver mixed pink. In the manufacturing industry has for the user.

This study aims to development of production process of hard metal by tungsten carbide powder with the particle sized of 0.1 - 0.35 µm. This carbide powder were made of recycling cemented carbide tool scraps so it is mixed with Ta = 2.82 % Mo = 0.45 % Nb = 1.22 % Ti = 4.56 % Zr = 0.37 % The shape of the carbide powder are roughly round due to ball milling for 300 hours. It was mixing cobalt 10 % and Paraffin wax 2 % which is found the work piece that running through the process of sintering with a temperature of 1400 °c and 1430 °c have the hardness of 1368.5 and 1346.3 HV respectively. In one hour of holding time process the work piece with 1430 °c of the sintering causes less wear. After the test of turning operation it can be concluded that the tungsten carbide cutting tool provides the equivalent quality as a standard cutting tool.

This research aims to produce scrap page kaolin of brick construction. The kaolin clay ratio of 100: 0 80:20 60:40 50:50 40:60 20:80 and 0: 100 by volume Add mixed with rice husk and rice 15 percent by weight A total of seven ratios. According to standard tests or TIS. 77-2545 ordinary story brick building. The moisture content and water absorption is increasing. While density Thermal conductivity resistance flexural and compressive strength tends to decrease. The best ratio of 80:20 by volume with compressive strength 43.16 kg / cm 2 and 24.93 percent water absorption. Criteria standard of TIS. 77-2545 requiring compressive strength not less than 35 kg / cm2 and water absorption must not be higher than 25 percent. Can be used in the manufacture of brick construction including building decorative wall can be developed into products. Because skin color and beautiful