The purpose of this research is to improve the physical and mechanicalqualities of natural rubber latex tiles. Water: surfactant: surfactant: 1: 2.75: 0.03: 0.30:0.03: 0.04 by weight and added with natural latex. In the ratio of Portland Cement Type 1: Natural Latex is 1: 0 1: 0.025 1: 0.05 1: 0.075 and 1: 0.10. Formed with compression presses at normal temperatures it was found that the optimum amount of natural latex For concrete reinforced concrete tiles the ratio is 1: 0.025. The tests in accordance with Thai Industrial Standard TIS 535-2556 are tested in 4 aspects. Dimensional stress test Water absorption test And waterproofness testing The value has passed the benchmark. And low thermal conductivity. Increasing the insulation of the roof as well. Can be used as a prototype product tile concrete roof natural latex. To produce commercially And there can be many local latex or rubber latex. To be more useful and valuable.

The objectives of this research are to study the production to find the proper ratio to test the physical mechanical properties and thermal conductivity to suggest the implementation and to transfer the technology of light-weight precast concrete wall panel product with adding high density foam sheet. The light-weight precast concrete wall panel product was produced by covering the foam sheet with steel pouring the mortar (M3 ratio which was proper ratio) and curing the light-weight precast concrete wall panel product. From the testing results followed the TIS.2226-2548 and TIS.878- 2537 the general characteristic of light-weight precast concrete wall panel product was perfect. The properties of light-weight precast concrete wall panel product include 17.81 MPa of compressive strength no bending when installed in common behavior 11.38% of water absorption passed in type1 of hardness and impact test 956.03 kg/m3 of density 9.18 MPa of bending strength and 0.170 watt/m.K of thermal insulation. This light-weight precast concrete wall panel product can use as the thermal insulation wall in building. Moreover the developing product can apply to register the petty patent.

The objectives of this research are to study the production to find the proper ratio to test the physical mechanical properties and thermal conductivity to suggest the implementation and to transfer the technology of l ight-weight precast concrete wall panel product with aerated foam injection technique as core wall. The light-weight precast concrete wall panel product was produced by casting the mortar panels with M3 ratio (proper ratio) set up the steels and injecting the aerated foams. From the testing results followed the TIS.2226-2548 and TIS.878-2537 the general characteristic of light-weight precast concrete wall panel product was perfect. The properties of light-weight precast concrete wall panel product include 17.81 MPa of compressive strength no bending when installed in common behavior 11.38% of water absorption passed in type1 of hardness and impact test 1110.58 kg/m3 of density 9.18 MPa of bending strength and 0.186 watt/m.K of thermal insulation. This light-weight precast concrete wall panel product can use as the thermal insulation wall in building. the developing product can apply to register the petty patent.

The objectives of this research are to study the production to find the proper ratio to test the physical mechanical properties and thermal conductivity to suggest the implementation and to transfer the technology of light-weight precast concrete wall panel products mixed with container foam wastes. Design the ratios of Portland cement type1: coarse sand: lime stone: water equal to 1: 2: 4: 0.7 by weight and adding the container foam wastes equal to 0 0.025 0.050 0.075 and 0.1 by weight. Casting the light-weight precast concrete wall panel products by pouring the concrete into the mold which installed the steels. Test the properties follow TIS.2226-2548 and TIS.878-2537. From the results the proper ratio of adding container foam wastes was 0.075 by weight which had perfect general characteristic 16.48 MPa of compressive strength no bending when installed in common behavior 8.86% of water absorption passed type1 of hardness test passed type 2 of impact test 2014.54 kg/m3 of density 4.30 MPa of bending strength and 0.228 watt/m.K of thermal insulation. This light-weight precast concrete wall panel product can use as the thermal insulation wall in building. Moreover the developing product can apply to register the petty patent.

This study aims to development of production process of hard metal by tungsten carbide powder with the particle sized of 0.1 - 0.35 µm. This carbide powder were made of recycling cemented carbide tool scraps so it is mixed with Ta = 2.82 % Mo = 0.45 % Nb = 1.22 % Ti = 4.56 % Zr = 0.37 % The shape of the carbide powder are roughly round due to ball milling for 300 hours. It was mixing cobalt 10 % and Paraffin wax 2 % which is found the work piece that running through the process of sintering with a temperature of 1400 °c and 1430 °c have the hardness of 1368.5 and 1346.3 HV respectively. In one hour of holding time process the work piece with 1430 °c of the sintering causes less wear. After the test of turning operation it can be concluded that the tungsten carbide cutting tool provides the equivalent quality as a standard cutting tool.