This research aims to study how to use stones Pumice Products is interlocking block for community development. The mixture ratios of Portland cement type1: sand: quarry dust: pumice rock fragments: water that there are 5 ratios. The products were tested by the community TCPS 602-2547 (2004) (Thai): interlocking block. The results showed that interlocking block of stone pumice much a compressive strength and thermal conductivity under a block of stone pumice less. The water absorption is increased When a block of stone pumice much. The optimum ratio and the use of waste rock Pumice highest ratio of cement to stone dust on the stone Pumice water in a 10: 6.4: 0.6: 0.45 to 10: 6.1: 0.9. 0.45 by weight.

การวิจัยนี้เป็นการศึกษาพฤติกรรมการอบชุบด้วยกระบวนการทางความร้อนของโลหะเงิน เจือต่ำ58.45wt%Ag +41.55wt%Cu โดยทำการเปรียบเทียบกับสมบัติของโลหะเงินสเตอร์ลิง 925 และโลหะเงินเจือต่ำ 58.33% เพื่อศึกษาสภาวะที่เหมาะในหาการปรับปรุงคุณสมบัติเชิงกลและโครงสร้าง จุลภาคของโลหะเงินเจือต่ำที่เป็นไปตามมาตรฐานผลิตเครื่องประดับ ผลจากการศึกษาโลหะเงิน 58.33 % ที่อัตราส่วนผสม 58.33Ag+36.66Cu+5.01Sn ซึ่งมี ค่าคุณสมบัติเชิงกลจากการทดสอบเบื้องต้นมีค่าเหมาะสมที่สุด จากนั้นท่าการศึกษาค่าความแข็งแรงดึง สูงสุดแบบเส้นลวดพบว่ามีค่าความต้านทานแรงดึงสูงสุดเท่ากับ 0.36 MPa ค่าเปอร์เซ็นต์การยืดตัว 0.11% เมื่อท่าการอบที่อุณหภูมิ 650 °C เวลาในการอบ 10 นาที ซึ่งปล่อยให้ชิ้นงานเย็นตัวในอากาศที่ อุณหภูมิห้องปกติ และค่าความแข็งจากการทดสอบมีค่าสูงสุดเท่ากับ 105.12 HV อบที่อุณหภูมิ 600 °C เวลาในการอบ 10 นาที ซึ่งปล่อยให้ชิ้นงานเย็นตัวในอากาศที่อุณหภูมิห้องปกติ ศึกษาโครงสร้างจุลภาค ของโลหะเงินเจือต่ำ 58.33Ag+41.57Cu+0.10Sn เมื่อท่าการอบปรับปรุงคุณสมบัติทางความร้อนและการ ชุบแข็งแบต่างๆ พบว่าโครงสร้างจุลภาคของชิ้นงานทดสอบหลังปล่อยให้เย็นตัวในอากาศ เกิดการ เปลี่ยนแปลงจาก β phase ที่มีขนาดเล็กลงเป็นโครงสร้าง Eutectic phase ที่มี α -phase และ β - phase ขนาดเล็กและละเอียด ซึ่งมีลักษณะสอดคล้องกับโครงสร้างจุลภาคของเฟสไดอะแกรมสมดุลโลหะ เงิน-ทองแดง ผลจากการทดลองและวิเคราะห์หาค่าคุณสมบัติเชิงกลของชิ้นงานทดสอบและโครงสร้างจุลภาค ที่ได้จากการทดลองในสภาวะต่างๆ มีค่าที่เป็นไปตามมาตรฐานของเครื่องประดับเงินตามมาตรฐาน อุตสาหกรรมการผลิตเครื่องประดับ ทั้งของในประเทศและต่างประเทศ

The objective of this research is to propose a new way to fabricate a composite material for future bone replacement development via growing apatite crystal on silk fibroin fiber. Apatite crystallization on silk fibroin fiber was prepared by precipitation reaction between Ca(NO3)2 solution and (NH4)2HPO4 solution adjusted pH by NH4OH solution. In this work Effect of solution concentration and initial pH values was investigated on apatite crystals. Chicken eggshells were used as calcium source by heating sufficiently powdered eggshells at 1300 °C for 4 h to acquire CaO powders made Ca(NO3)2 solution by dissolving in 65% HNO3 solution. Prepared Ca(NO3)2 solutions were adjusted concentration as 3 levels and were adjusted different pH values of 7 8 and 9 respectively. For processing of apatite crystallization silk fibroin fibers were immersed in Ca(NO3)2 solutions for 30 min. After that (NH4)2HPO4 solutions were added in silk fibroin fibers immersed in Ca(NO3)2 solutions. Reaction time was fixed about 1 min before cleaning to remove impurity precipitates on surface of silk fibroin fiber. Finally apatite crystallization on silk fibroin fibers occurred. The obtained result can conclude morphologies of apatite crystals on silk fibroin fibers was sheets sphere and flower. Solution concentrations and initial pH values directly influenced on Ca/P ratio of obtained apatite crystals by Ca/P ratio increases as increased solution concentrations or increased pH values. Finally research silk fibroin fibers were woven as two patterns of plain weave and twill weave and they were investigated Young’s modulus and tensile strength. The result indicates that Young’s modulus of silk fibroin fiber sheets woven as twill weave and as plain weave were about 616 MPa and 425 Mpa and tensile strengths of them weave were about 40 Mpa and 72 Mpa respectively. The optimum condition of growing apatite crystals on silk fibroin fibers was sample of CP19. Design of silk fibroin fiber with plain weave was an optimum pattern for future biomedical applicaions.

The effect of azimuth and pot color on the variation of pot surface and growing media temperature was studied. Four pot colors that including with black brown silver and white color were used. The growing media comprised with soil : rice husk : coconut dust at 1:1:1 ratio. From the result of this study the azimuth and pot color effected the variation of pot surface temperature. The azimuth effected the variation of pot surface temperature at 8.00 10.00 14.00 and 16.00. At 8.00 and 10.00 pot surface temperature in east direction was the highest while at 14.00 and 16.00 pot surface temperature in west direction was the highest. Whereas pot color effected the variation of pot surface temperature at 8.00 10.00 and 14.00 with black color was the color that had the highest 33.3 39.1 and 46.4 C respectively. On the other hand the white color was the color that could the highest reduces the pot surface temperature when compared with the temperature of black pot color which were 4.6 3.9 and 4.3 C lower than that in a black pot respectively. Not only the effect on the variation of pot surface temperature pot color was also affected on the variation of growing media. Pot color effected the variation of growing media temperature during 8.00 to 18.00. When compare the growing media temperature among the pot color with that in black pot color which was the highest temperature white color pot was the highest efficiency to reduce the growing media temperature especially at 10.00 and 12.00. White pot color could reduce the growing media temperature about 5 C follow by silver color pot was about 3 C while the growing media temperature in brown color pot was not difference with that in black color pot

Honey-nanofibers were fabricated by electrospinning technique in order to study their potentiality for biomedical application especially as wound healing materials. Honey/Gelatin ratios operating voltages and solution flow rates were considered as the experimental variables. All synthesized nanofibers were tested for their sizes percentages of water uptake and contact angles between the fiber surfaces and water droplets. It was found that 1) size of nanofibers and contact angle between the fiber surfaces and water droplet increased with increasing of honey in solution 2) size and percentage of water uptake of nanofibers increased with stepping up of operating voltage and 3) size of nanofibers was minimized at the flow rate of 0.06 ml/hr for each operating voltage of this study.