This study aims to development of production process of hard metal by tungsten carbide powder with the particle sized of 0.1 - 0.35 µm. This carbide powder were made of recycling cemented carbide tool scraps so it is mixed with Ta = 2.82 % Mo = 0.45 % Nb = 1.22 % Ti = 4.56 % Zr = 0.37 % The shape of the carbide powder are roughly round due to ball milling for 300 hours. It was mixing cobalt 10 % and Paraffin wax 2 % which is found the work piece that running through the process of sintering with a temperature of 1400 °c and 1430 °c have the hardness of 1368.5 and 1346.3 HV respectively. In one hour of holding time process the work piece with 1430 °c of the sintering causes less wear. After the test of turning operation it can be concluded that the tungsten carbide cutting tool provides the equivalent quality as a standard cutting tool.

WC powder was obtained from recycling cemented carbide scraps. This metal power contained tungsten carbide (WC) at 89.17% titanium (Ti) at 4.90% tantalum (Ta) at 3.56% niobium (Nb) at 1.31% and molybdenum (Mo) at 0.93%. Its particle size and distribution was in the range of 0.03-85.31 µm. After quality improvement of the metal powder by ball milling screening and separating the compounds the result showed that the particle size of the metal powder was decreased to 0.01-0.10 µm (10-100 nm). The average size of the powdered particle was 28 nm. The tungsten powder was in more perfect condition by 95.85%

This research was on the production of hardmetal from recovery of tungsten carbide tool scraps recycling through ball milling for 40 hours. The metal powder obtained which was of the size between 0.11-0.22 µm was composed of 96.69% of tungsten carbide (WC) 1.68% of tantalum (Ta) 1.21% of titanium (Ti) and 0.42% of niobium (Nb). When mixed with 5-15% cobalt binder metal cold isostatic press (CIP) sintered at 1450 ° C it became hardmetal work piece dimension 12.39 x 13.82 x 5.60 mm with 1410 HV hardness and 14.34 g/cm3 density. The result of S45C steel turning was tools life good. The research concluded that the hardmetal work piece produced by the developed material had suitable basic specification and would lead to the development in working in the future.